Pigmented Epoxy Mortar Resin Product #24 is a multipurpose colored epoxy binder for Epoxy Mortar Systems. This all purpose epoxy resin is characterized as an excellent general purpose material with good clarity and color retention. It is essentially odorless and can therefore be used in occupied areas. Pigmented Epoxy Mortar Resin Product #24 is 100% solids and has Zero (0) VOC, so it meets event the strictest low VOC standards.
100% solids amine cured Epoxy Resin and Epoxy Hardener.
SURFACE PREPARATION
Surface Preparation is the most critical portion to any successful resinous flooring system application. All substrates to receive Pigmented Epoxy Mortar Resin Product #24 must be properly prepared as outlined in Epoxy Surface Preparation Procedures. Epoxy.com technical service department is pleased to answer any questions.
INSTALLATION
Will vary with application method.
PHYSICAL PROPERTIES |
|
| Color | Light Grey, Taupe, Sand, Dark Grey, Old Gold, Slate Blue, Mocha, Colonial Green, Brick Red, Deep Blue, White. Black, Safety Yellow |
| Gloss, 60�F | 85-1 00 |
| Weight/gallon | 9.00-9.5mixed |
| Solids Content | 100% |
| Mix Ratio | 4A to I B by volume |
| Pot Life | 30-40minutes @ 70°F |
| Viscosity | 950 cps, mixed approx. |
| VOC | 0 |
| 10-20 mil film | 10-14 hrs. |
| Light Traffic | 16 hrs. |
| Ultimate Cure @ 74°F | 5 days |
| Dry Time @ 50°F | 14 days |
Click
the picture of color card below for a larger version of this picture
of the color chart.
Please note: The picture to the right is a photographic reproduction of the
color card for this product. The photo reproduction process and your
monitor and/or printer will change these colors. This chart is to give you
an idea of the colors available and not intended for critical color selections.
REAGENT |
RATING |
REAGENT |
RATING |
| Acetic Acid-5% | L | Lactic Acid-15% | R |
| Acetone | L | Methyl Ethyl Ketone | L |
| Bleach | L | Nitric Acid-10% | R |
| Citric Acid-30% | R | Skydrol | R |
| Crude Oil | R | Sodium Hydroxide-50% | R |
| Diesel Fuel | R | Sulfuric Acid-20% | R |
| Ethylene Glycol | R | Toluene | R |
| Fatty Acids | L | Urea | R |
| Gasoline | R | Vinegar | L |
| Hydrochloric Acid-15% | R | Xylene | R |
PERFORMANCE PROPERTIES |
|
| Tensile Strength ASTM-D-638 | 8500 psi |
| Elongation ASTM-D-638 | 5.5% |
| Adhesion to metal | 2500 psi |
| Adhesion to concrete ACI Committee 403 | 350 psi (concrete fails) |
| Hardness ASTM-D-2240 | 80 (Shore D) |
| Abrasion Resistance ASTM-C-501 | 35-40 mg loss (CS-17 wheel, 1 kg load, 1000 cycles) |
| Service Temperature MIL- D-3134F | 160 F (immersion) 185 F (dry heat) |
| Impact Resistance MIL-D3134F � 4.7.3 | Withstands 16ft/lbs. no cracking, delamination or chipping. |
| Indentation MIL-D-3134F �4.7.4 | Withstands 2,000 lbs./sq. in. for 30 min. without indentation. |
| Elevated Temperature Resistance MIL-D-31 34F �4 7 5 |
No slip or flow at required temperatures at 158°F |
| Water Absorption ASTM-D-670-63 (24. hr. immersion) | 0.10% maximum |
| Flexural Strength ASTM-D-790 | 8,000 psi |
| Compressive Strength ASTM-D-695 | 11,000 psi |